The SWNT-based SA preparation is similar to the processes reported in Refs^29,59. We disperse ~0.03 wt.% laser ablation SWNTs (~1.3 nm mean diameter)⁶⁰ in deionized water with ~0.7 wt.% sodium-carboxymethycellulose (Na-CMC) polymer. In comparison with the commonly used host polymer of polyvinyl alcohol (PVA), Na-CMC can function as both dispersant and host polymer for free-standing SWNT-SA fabrication⁶¹. Further, Na-CMC is more stable and has higher transmittance at 1.5 μm than PVA as PVA has strong moisture absorption²⁹. The choice of SWNTs ensures a broad absorption peak near 1.55 μm^62,63, measured with UV-Vis spectrophotometer (Fig. 1a). The sonication is carried out for one hour using a tip sonicator (Branson 450A, 20 kHz) with ~50 W power at room temperature. The as prepared dispersion does not exhibit any visible SWNT aggregates. This is then centrifuged in a swing bucket rotor at 30 k rpm using an Optima-Max-E ultracentrifuge (Beckman Coulter) to filter out the residual bundles and impurities. The top ~70% of the dispersion (~6 ml) is decanted for composite fabrication. Slow evaporation of water under ambient temperature for one week produces a free-standing SWNT-CMC SA.Figure 1

(a) Optical absorption spectrum of our SWNT-CMC polymer composite film (pink rectangular area indicates our operation laser wavelength range). (b) Transmittance of the film as a function of the input intensity.

A schematic of the laser setup is shown in Fig. 2. A segment of ~0.8 m EDF is used as the gain medium, which is pumped through a 980/1550 nm fused fiber wavelength division multiplexer (WDM) by a 980 nm laser diode (LD). A polarization independent isolator (ISO) is connected subsequently to ensure unidirectional propagation of the light in the circular cavity. A polarization controller (PC) is used to optimize the laser mode-locking operation by adjusting the state of polarization. The SWNT-CMC polymer composite film is sandwiched between two fiber connectors to form an all-fiber integrated SA device. The intracavity light is extracted via the 10% port of a 10/90 fiber coupler. To investigate the wavelength and pulse duration tunability in the mode-locking scheme, a tunable bandpass and wavelength filter (TBWF, PriTel) is employed to selectively control the output pulse performance in wavelength and time domains. Tuning the tilt angle of the filter by rotating two adjustable micrometer screws controls the central wavelength and the spectral bandwidth. The bandwidth of the transmission spectrum can be varied with symmetric enlargement and compression of the filter passband. Figure 3(a) shows the typical transmission spectra with different FWHMs from 1 nm to 11 nm with the central wavelengths fixed at 1559 nm (the maximum wavelength available with our filter). Note that similar bandwidth variable transmission spectra are also available if the central wavelength is tuned to smaller values but larger than 1541.5 nm. Wavelength tuning of the transmission spectrum with fixed profile is a result of the filter passband edges moving along the same direction. The maximum tunable range is acquired for 35 nm (1524–1559 nm) when the bandwidth is compressed to ~1.2 nm, as shown in Fig. 3(b). These experimental results demonstrate the TBWF is an effective tool for independent bandwidth and wavelength tuning.Figure 2

The schematic setup of the mode-locked fiber laser. LD, laser diode; WDM, wavelength division multiplexer; EDF, Erbium doped fiber; ISO, polarization independent isolator; PC, polarization controller.

Mode-locked laser performance of the cavity without the TBWF is first characterized. CW laser output is obtained when the pump power reaches ~5.3 mW. When the pump power is further increased to ~17.1 mW, the CW light is converted to a mode-locked pulse train with an output power of ~1.26 mW. To stabilize the pulse train, intracavity birefringence needs to be modified by adjusting the intracavity PC. After, stable mode-locking is well maintained without adjustment of PC, even when we further increase the pump power or tune the filter. Stable CW mode-locking operation is observed in a pump power range of 17.1–56.9 mW. Figure 4 shows the output laser performance measured at the pump power of 33 mW. The laser mode-locks at the central wavelength of 1560.5 nm, with a full width at half maximum (FWHM) of ~6.7 nm; Fig. 4(a). The sidebands (located at 1539.78 nm, 1546.58 nm, 1574.58 nm and 1581.38 nm) confirm a soliton-like mode-locking, revealing a typical character of anomalous dispersion cavities⁶⁴. Figure 4(b) depicts the measurement results of the pulse duration, which can be well-fitted to a sech² temporal profile. The autocorrelation trace implies an FWHM pulse duration of 495 fs. The time bandwidth product (TBP) of the soliton-like pulse is 0.408, slightly larger than the sech² transform-limited TBP value of 0.315. This indicates that the output pulses are slightly chirped.Figure 4

(a) Output spectrum and (b) pulse duration measurements of the mode-locked laser without TBWF.

The pump power range associated with stable mode-locking operation increases when the filter is inserted in the cavity. However, to compare the laser performance, we measure the wavelength tunability results (Fig. 5) at a pump power of 33 mW. Output wavelength of the mode-locked laser is tuned for a 34 nm span, covering the range from 1525 nm to 1559 nm as shown in Fig. 5(a). FWHMs of all the output spectra are ~1.2 nm, which are approximately half of the filter bandwidth. This is consistent with the previous ultrafast fiber laser demonstration with an intracavity filter⁶⁵. These broad wavelength tunable results confirm the wide operation bandwidth of the demonstrated SWNT-based SA. Noting that the experimentally acquired tuning range is limited by the passband width of the TBWF (see Fig. 3(b)). Therefore, a tunable wavelength span larger than 34 nm is also possible. Figure 5(b) plots a representative pulse duration measurement, the sech² fitting result gives a pulse duration of 6.1 ps, which is the longest pulse generated in this laser (corresponding to the narrowest spectral bandwidth of 1.2 nm). In further investigation, we intentionally enlarge the spectral bandwidth in the available range and then investigate the tunability of central wavelength at fixed bandwidth. The results demonstrate that the spectral bandwidth can be continuously changed between 1.2 and 6 nm (limited by the filter bandwidth tuning range of ~2 nm and 11 nm). Figure 5(c) shows the experimentally measured spectra of the continuously tuned laser from 1541.5 nm to 1562.6 nm with a maximum bandwidth of 6 nm. The measured autocorrelation trace in Fig. 5(d) gives a pulse duration of 545 fs, which is longer than the pulse (495 fs) without filtering. This expected pulse duration extension is attributed to the spectral filtering and anomalous dispersion increase caused by the TBWF and its fiber pigtail.Figure 5

Wavelength tunability of the mode-locked fiber laser. (a) Mode-locked laser output spectra for a 34 nm span, FWHMs of the output spectra are ~1.2 nm. (b) Second harmonic autocorrelation trace of mode-locked pulse at 1545 nm wavelength. (c) Output spectra over a 21.1 nm span. FWHMs of the output spectra are 6 nm. (d) Second harmonic autocorrelation trace of mode-locked pulse at 1544.8 nm. (e) Output pulse train (corresponding to a repetition rate of 17.4 MHz). (f) Radio frequency spectrum at the fundamental repetition rate of f₀ (f₀ = 17.4 MHz) with 100 Hz resolution bandwidth. Inset: broadband frequency spectrum (up to 1 GHz) with 100 kHz resolution bandwidth.

The spectral bandwidth can be readily tuned by controlling the passband of the TBWF. Our experimental observation shows that the FWHM of the mode-locked output spectral bandwidth is continuously tunable from the maximum value of 6 nm to the minimum of 1.2 nm. The slight reduction of the maximum bandwidth (from 6.7 nm to 6 nm) is caused by the unavoidable spectral filtering from the TBWF. Upon further tuning the spectral bandwidth to <1.2 nm, the mode-locking pulse train becomes unstable and finally collapses. This is due to the rise of intracavity loss from a strong wave filtering⁶⁶ as the passband of the filter is compressed. Figure 6(a) performs the mode-locked output spectra with bandwidths of 1.2, 2, 3, 4, 5, and 6 nm centered at the same wavelength of 1559 nm. It is noteworthy to mention that such large spectral bandwidth tuning (from 1.2 nm to 6 nm) at peak wavelengths shorter than 1541.5 nm (e.g., 1530 nm) is not achieved in our experiment, possibly due to the gain filtering effect. To investigate the relationship between the output spectral bandwidth and the pulse duration, we measure the autocorrelation traces of the mode-locked pulses at different bandwidths obtained in Fig. 6(a). The corresponded results are plotted in Fig. 6(b). The pulse durations as a function of the respective spectral bandwidth are then analytically shown in Fig. 6(c) (blue spheres). We also theoretically calculate the pulse duration Δτ with the following formula \documentclass[12pt]{minimal} \usepackage{amsmath} \usepackage{wasysym} \usepackage{amsfonts} \usepackage{amssymb} \usepackage{amsbsy} \usepackage{mathrsfs} \usepackage{upgreek} \setlength{\oddsidemargin}{-69pt} \begin{document}$${\rm{\Delta }}{\rm{\tau }}=\tfrac{{\lambda }^{2}}{c\cdot {\rm{\Delta }}\lambda }\times 0.315$$\end{document}Δτ=λ2c⋅Δλ×0.315, where Δτ is the pulse duration, λ the central wavelength (i.e., 1559 nm), c the velocity of light in vacuum and Δλ the FWHM of the output spectrum. It can be seen that the experimental pulse duration results corresponding to the 3 nm, 4 nm, 5 nm and 6 nm spectral bandwidth are quite close to the transform limited values at the sub-picosecond range (shown in red, Fig. 6(c)). However, when the output spectral bandwidth is further reduced to 2 nm and 1.2 nm, the experimental pulse durations are longer than that of the transform limited values. This TBP fluctuation is caused by the variations of a few factors including the filter bandwidth and the optical and cavity dispersion⁵⁶. The flexible and large range wavelength and pulse duration tunability in our experiment provides a new approach for developing novel ultrafast source. SWNT polymer composite SA and in-line tunable filter play the key roles for tunable pulse generation in a compact and environmentally insensitive fiber cavity. Note that the wavelength and pulse duration tunable fiber laser design is also applicable to other nanomaterial⁶⁷ optical switch based fiber lasers (e.g., graphene^{29,33–43,68}, black phosphorus^69–72, MoS₂^36,73–76, WS₂^74,77, MoSe₂^74,78, WSe₂⁷⁹, and their heterostructures^35,80).Figure 6

Pulse-duration tunable mode-locked output performance. (a) FWHM bandwidth tunable from minimum 1.2 nm to maximum 6 nm with a symmetric distribution at central wavelength of 1559 nm. (b) Pulse duration measurement corresponding to different spectral bandwidths. (c) Output pulse duration as a function of spectral FWHM. Blue spheres show the experimental value, red curve indicates the transform limited pulse durations.

The datasets generated during the current study are available from the corresponding author on reasonable request.